电弧喷涂不锈钢工艺对涂层孔隙率和氧化物含量的影响

伞金福; 杜智; 毕志夫

引用本文:	伞金福,杜智,毕志夫.电弧喷涂不锈钢工艺对涂层孔隙率和氧化物含量的影响[J].中国表面工程,1997,(3):
	.Effect of Spraying Parameters on Porosity and Oxides Content of Arc-sprayed Stainless Steel Coatings[J].China Surface Engineering,1997,(3):

【打印本页】【HTML】【下载PDF全文】【查看/发表评论】【EndNote】【RefMan】【BibTex】

←前一篇|后一篇→

过刊浏览高级检索

本文已被：浏览 4811次下载 81次
电弧喷涂不锈钢工艺对涂层孔隙率和氧化物含量的影响
伞金福,杜智,毕志夫

作者

单位

摘要:

本文利用OMNICON5000图像分析仪测定了电弧喷涂3Cr13和1Cr18Ni9Ti不锈钢涂层的孔隙率和氧化物含量，考察了喷涂工艺参数对其影响。研究结果为正确控制电弧喷涂工艺提供了实验依据。

关键词: 电弧喷涂,不锈钢涂层,孔隙率,氧化物

DOI：

分类号:TG17

基金项目:

Effect of Spraying Parameters on Porosity and Oxides Content of Arc-sprayed Stainless Steel Coatings

San Jinfu, Du Zhi Tsing Hua UniversityBi Zhifu He Bei Research Center of Surface Technology

Abstract:

In this paper, the porosity and oxides content ofArc - sprayed 3Cr13 and 1Cr18Ni9Ti Stainless Steel Coatings were tested by an OMNICON5000 medel image ana-lyzer, and effect of spraying parameters on them was stud-ied. The research result provides experimental basis forcontrolling are spraying process precisely.

Key words: Are spraying, Stainless Steel, Coatings Porosity, Oxides